Partes Ceramicae Aluminae Altae Puritatis ad Usus Semiconductorum et Industriales
St.Cera partes ceramicas ex alumina (Al₂O₃) accurate machinatas ad specificationes emptorum fabricat. Hae partes, alumina altae puritatis 99.8% utentes, praebent excellentem firmitatem flexuralem (361 MPa), magnam duritiem (16 GPa), et eximiam firmitatem dielectricam (15×10⁶ V/m). Ad apparatum semiconductorum, coetus attritioni resistentes, insulatores electricos, et lumina altae temperaturae destinatae, materia absorptionem aquae fere nullam (0%) et coefficientem expansionis thermalis 7.2×10⁻⁶/℃ praebet, stabilitatem dimensionalem sub condicionibus extremis praestans.
Specificationes(fundatum in 99.8% Al)₂O₃):
Possessio | Valor |
| Materia | 99.8% Alumina (Ebur) |
| Densitas | 3.93 g/cm³ |
| Robur Flexurale | 361 MPa |
| Robustitia Fracturae | 3–4 MPa·m¹/² |
| Duritia Vickersiana | 16 GPa |
| Modulus Youngi | 380 GPa |
| Conductivitas Thermalis | 32 W/m·k |
| Expansio Thermica (25–1000°C) | 7.2×10⁻⁶/℃ |
| Constans Dielectrica | 9.6 |
| Angulus Amissionis Dielectricae | 0.0001 |
| Robur Dielectricum | 15×10⁶ V/m |
| Resistentia Specifica | >10¹⁴ Ω·cm |
| Temperatura Operativa Maxima | 1600°C |
Applicationes:
- · Tegumenta camerae processus semiconductoris, fenestrae, et laminae distributionis gasis
- · Bucci, anuli obturantes, et sphaerae ferreae resistentes attritioni
- Insulatores electrici altae tensionis et insulatores candelarum ignitoriarum
- · Instrumenta furni, fulcra calefactoria, et tubi protectionis thermocouple
Processus Fabricationis:
Pressio isostatica → machinatio "viridis" → sinterizatio ad 1600°C → trituratio / laminatio accurata CNC → purgatio ultrasonica → inspectio dimensionalis CMM 100%. Geometriae complexae, parietes tenues (≥0.5 mm), et tolerantiae strictae (usque ad ±0.01 mm) regulariter assequuntur.
Qualitatis Moderatio:
Certificatum secundum ISO 9001:2015. Quaeque series examinatur pro robore flexurali (flexura trium punctorum), duritie (Vickers), robore dielectrico (ASTM D149), et resistentia contra impetum thermalem (10 cyclos, 25°C ↔ 1000°C). Nullae fissurae aut laesurae sub microscopio 20× visibiles.
Commoda prae partibus metallicis vel polymericis:
- · 3–5× durior quam chalybs inoxidabilis (16 GPa contra ~2 GPa)
- · Chemicaliter iners — resistens acidis, alcalibus, et halogenis (praeter HF)
- · Insulator electricus >10¹⁴ Ω·cm, usum in ambitu altae tensionis permittit
- · Servitium continuum usque ad 1600°C, limites metallorum vel materiarum plasticarum longe excedens
Adaptatio:
Delineationes emptorum (forma STEP/IGS) accipimus et prototypa celeriter fabricari (duas vel tres hebdomades) offerimus. Partes sinterizatae, tritae, lappatae, vel politae (Ra ≤0.05 μm) praeberi possunt. Rotundatio marginum, foramina contraiacta, foramina filetata, et sulci vacui praesto sunt.
Nota: Pro applicationibus quae maiorem tenacitatem fracturae requirunt, partes zirconiae (ZrO₂) considera. Pro maxima conductivitate thermali, ad nostra producta BeO vel Si₃N₄ refer. Omnia data supra stricte tabulam proprietatum Al₂O₃ datam sequuntur (gradus 99.8%).